Grade 23 Titanium Rod has good physical and chemical properties, low density, lightweight, non-magnetic, high strength, and good corrosion resistance. They have good mechanical properties and welding performance. medical titanium rod is widely used in chemical equipment and seawater. Desalination, marine parts, electroplating industry, etc. Titanium is 10 times more corrosion resistant than ordinary stainless steel, and titanium metal is a metal with relatively low body rejection, so the processed parts of titanium rectangular rod are widely used in human implants and medical devices use.
skills requirement:
1. The chemical composition of titanium and titanium alloy bars shall comply with the provisions of GB / T 3620.1, and the tolerance deviation of the chemical composition shall comply with the provisions of GB / T 3620.2 when the buyer re-inspects.
2. The diameter or side length of the hot-processed bar and its allowable deviation should meet the requirements of Table 1.
3. After hot working, the diameter of the cold-drawn bar and the cold-rolled bar and cold-rolled bar should be in accordance with the requirements of Table 2.
4. The out-of-roundness of the bar after turning (grinding) after hot processing should be no more than half of its dimensional tolerance.
5. The length of the indeterminate length of the processed bar is 300-6000mm, and the length of the annealed bar is 300-2000mm. The length of the fixed-length or double-length should be within the range of the indefinite length.
skills requirement:
1. The chemical composition of titanium and titanium alloy bars shall comply with the provisions of GB / T 3620.1, and the tolerance deviation of the chemical composition shall comply with the provisions of GB / T 3620.2 when the buyer re-inspects.
2. The diameter or side length of the hot-processed bar and its allowable deviation should meet the requirements of Table 1.
3. After hot working, the diameter of the cold-drawn bar and the cold-rolled bar and cold-rolled bar should be in accordance with the requirements of Table 2.
4. The out-of-roundness of the bar after turning (grinding) after hot processing should be no more than half of its dimensional tolerance.
5. The length of the indeterminate length of the processed bar is 300-6000mm, and the length of the annealed bar is 300-2000mm. The length of the fixed-length or double-length should be within the range of the indefinite length.