Matters needing attention when processing titanium bolts

Titanium alloy materials are difficult to process materials, have poor thermal conductivity, are easy to adhere to tools, have strong notch sensitivity, and will produce strong work hardening during the rolling process. In actual production, there are a series of problems in the rolling of full profile.

First, after the full profile squeezes the gap between the two rolling wheels during rolling, if the rolling wheels continue to roll, the blank material has nowhere to flow and can only be squeezed back and forth between the rolling wheels. As a result, the thread has a higher surface hardening. F5 Titanium Forging the hardening exceeds the tensile limit of the material, cracks will occur. As shown in Figure 1, the thread flanks and tooth bottom harden the most, so cracks occur;

Second, during full extrusion, each tooth of the rolling wheel involved in rolling is also affected by a strong cyclic load. The energy of rolling also acts on the rolling wheel, causing its life to be seriously reduced. In production, each pair of thread rolling wheels can only roll 3000-5000 titanium bolts, resulting in the phenomenon of tooth crest fragmentation, and the thread rolling wheels can no longer be used, which is extremely expensive. In addition, the thread rolling wheel tooth crest is broken Titanium Grade 2 Round Bar is a forming process in the production, so that the producer cannot determine the eligibility of the rolled thread, that is, when the rolled thread is qualified and when the rolled thread is unqualified;

Third, in the process of rolling and forming the thread, the two sides rise the fastest. When the thread is full, a fold will be formed on the crest. During the inspection, there are fluorescent display marks on the crest of the thread. In order to determine the maximum defect depth, anatomy is required. The method can only determine whether the defect at this place exceeds the standard; fourth, modern fasteners have high fatigue life, and have high precision requirements for bolt holes, and no hole wall damage is allowed during the installation process. The sharper thread crest is very easy to damage the hole wall. In short, the full thread profile brings great trouble to production, which not only increases the chance of cracks, reduces the fatigue life of parts, but also reduces the service life of the rolling wheel. In addition, it brings unnecessary trouble to the inspection. It is easy to cause damage to the hole wall, so it is imperative to correct the major diameter of the titanium tube grade 9 alloy fastener thread.

What is a titanium flange?

The titanium flange is made of non-ferrous metal grade 2 titanium sheet or titanium alloy, which connects the pipe and the pipe to the end of the pipe. The titanium flange has holes, and the two flanges are tightened with bolts. Gasket between flanges. Flanged pipe fittings refer to pipe fittings with flanges (flanges or joints).

It can consist of threaded connection or welding. The flange joint consists of a pair of flanges, a washer and many bolts and nuts. The gasket is placed between the sealing surfaces of the two flanges. After tightening the nut, the specific pressure on the surface of the washer reaches a certain value and deforms. The surface of the gasket is filled with bumps on the sealing surface to ensure a tight connection.

According to the structure, there are flat welding titanium flanges, butt welding titanium flanges, threaded Gr23 Ti-6Al-4V ELI Titanium Foil, and blind titanium flanges.

Product specifications: Various specifications are produced according to flange standards, or non-standard flanges are produced according to drawings provided by customers.

Production methods: free forging, die forging, precision forging, and welding

Inspection method: X-ray inspection, color inspection, defect inspection, water pressure test and other tests can be carried out according to customer needs.

How to improve the welding regulations of titanium alloy titanium pipe joints

Because titanium alloy titanium tube is more open-minded, and when performing the welding of titanium alloy titanium tube, there are stricter regulations on the control of welding temperature, the actual effect of maintaining the maintenance of the steam, and the natural environment of the welding. It will cause great harm to the welding quality and will cause damage to the product when it is more serious. Practical experience: According to the development of various key factors that endanger the quality of welding, clarify the important whole process of welding, improve the manipulation of the natural environment, staff, and main welding parameters and methods in the whole process of welding, so as to reasonably ensure the quality of titanium pipe raw materials. Welding quality has been further improved to avoid the appearance of welding waste.

In recent years, a new type of Ti 6Al-2Sn-4Zr-6Mo Titanium Rod alloy titanium pipe fittings has been widely used. Because aluminum alloy has the characteristics and characteristics of light ratio, high compressive strength, corrosion resistance, etc., in addition to being widely used in aerospace, petrochemical equipment, and mechanical equipment manufacturing industries, it is also used for the first time in the pipelines of river ships at this stage. Under construction. However, because the aluminum alloy is a kind of metal material with strong cheerfulness, it has great infectious power to vapors such as oxygen, hydrogen, nitrogen, etc. at high temperatures, that is, the ability to digest, absorb and melt vapors is very strong, especially when facing welding In the whole process, this kind of ability is mainly manifested especially as the welding temperature rises. Practical experience, if the digestion, absorption, and melting of aluminum alloy and oxygen, hydrogen, nitrogen, and other vapors are not controlled during welding, it will eventually cause damage to the product. Therefore, in the welding of ERTi-23 Titanium Welding Wire pipe joints, reasonable prevention and manipulation must be made in many aspects to consider the quality regulations on welding.

How to improve the welding regulations of titanium alloy titanium pipe joints

Welding workers should wear clean-up work clothes, and there must be no oil stains. Welding gloves should use white sand cloth gloves, and it is prohibited to wear cotton rope and gloves made of other materials.

The welding service platform section and the wire brushes used in the welding area of ​​the welded joints should be made of stainless steel plates. Carbon steel and other environmentally polluting materials are prohibited.

The welding place should be set as far as possible in the room or in the middle of special welding work. Smoking is prohibited in the room. The natural environment should be kept clean and dry. The indoor temperature should not be less than 5℃, and the heat convection of the gas should be strictly controlled.

In order to better obtain a more ideal welding quality, try to produce and process the butt joint top into a V-shaped weld, and use toluene for deoiling the welding area and the surface of the electrode. 

Application of TC4 titanium alloy and TC11 titanium alloy in titanium materials in important fields such as chemical petroleum and electric power

Titanium and titanium alloys have low density and high tensile strength. In the range of -253-600 degrees Celsius, its specific strength is almost the highest among metal materials. In a suitable oxidizing environment, it can form a thin and hard oxide. The material film has excellent corrosion resistance. In addition, it is also non-magnetic and has a small linear expansion coefficient. This makes Gr9 Ti-3Al-2.5V Titanium Wire and alloys first known as important aerospace structural materials, and then they have also been popularized in shipbuilding, chemical industry and other fields, and they have developed rapidly. Especially in the chemical industry, more and more products are using titanium and titanium alloy products, such as petrochemical, fiber, pulp, fertilizer, electrochemical and desalination industries, as exchangers, reaction towers, synthesizers,

With the development of science and technology, the application fields of titanium are becoming more and more extensive, such as in medical, automobile, sports and other fields. Through these, titanium metric screw is also truly reflected as a light metal, and its properties are getting better and better. It has been recognized and repaired by people, and replaced other metals as soon as possible to integrate into our production and application fields, and even our body.

How magnetic is a titanium tube? what is the purpose?

Titanium rod barrel burnishing is to grind the parts and abrasives in dilute acid or dilute alkali with emulsifier (or corrosion inhibitor) and follow the rotation of the drum to obtain a bright appearance. It is suitable for the disposal of small parts and parts that are difficult to polish and polish. The correct selection of roller burnishing standards can improve productivity and quality.

(1) The shape of the roller

The shape of the roller is round, hexagonal and octagonal, among which the polygonal shape is good for practicality. This is because the radii of the barrel wall from the axis are not equal, and there is a certain point of view, so the rolling parts are easy to change the position, the chance of collision with each other increases, the grinding is uniform, and the efficiency is high, which can shorten the rolling time.

(2) The size of the drum

The direct alignment is 50mm-100mm, and the length varies with the number of grids. The length of the first pattern roller is 600-800mm; the second pattern is 800-1500mm. Usually the larger one is better. This is because the parts are subjected to high pressure and friction in the drum, so the amount of cutting is also increased. But for those parts that are afraid of being stressed and easily deformed, a small roller can be used and the length of the roller can be increased.

1) Data for roller

There is a direct relationship between the rotation speed of the drum and the scraping amount of the parts within a certain range, that is, the faster the rotation speed, the greater the scraping of the metal surface. However, when the speed exceeds a certain upper limit, it drops instead. Because when the rotating speed is too fast, the centrifugal force of the parts in the drum increases, which reduces the friction. Usually it is appropriate to control at 45r/min.

2) Abrasives and solutions for roller burnishing

Abrasives for rolling include pumice, quartz, titanium foil granite skin angles, shells, iron filings and ceramic fragments. The size of the abrasive particles should be larger or smaller than each hole of the Cen part. The amount of content in the drum is also an important factor affecting the quality of the agricultural surface of the parts. The amount of people inside the drum is usually 70% of the drum volume. Regarding heavier parts or threaded parts, the load should be controlled at 80%-90%. The solution in the drum should be added to about 95% of the drum volume (note: when adding acidic solution to the drum, you should first add enough water, and then add acid, to avoid corrosion of parts in the rolling process, because of the increase in time , The concentration of the built-in solution gradually decreases, grade 7 titanium alloy sheet or even loses its effect. Therefore, the concentration of the solution should be checked and replaced at regular intervals. The burn-in time should not be too long, otherwise the parts will be damaged. That is, use a brush to remove the surface of the parts. Burrs, terbium compounds, remaining oil and corrosion sludge, etc., and make the parts have a certain luster. Be sure to point out that elastic, rigid or thin-walled parts should be taken out in time after the finishing of rolling, otherwise it will easily cause hydrogen seepage or local over-corrosion .

What are the characteristics of seamless titanium tube?

1. As an emerging material, astm b348 titanium rod has been used in the pharmaceutical industry, surgical instruments, human implants and other fields in my country and the world for decades, and has achieved great success.

2. Bone and joint injuries caused by trauma and tumors in the human body, artificial joints, bone plates and screws can be made from Gr9 Ti-3Al-2.5V Titanium Foil and titanium alloys and are now widely used in clinical practice. It is also used in hip joints (including femoral heads), knee joints, elbow joints, metacarpophalangeal joints, interphalangeal joints, mandibles, artificial vertebral bodies (spine orthoses), pacemaker housings, artificial hearts (heart valves), Artificial dental implants, and Grade 36 Titanium Bar mesh are used in cranial plastic surgery.

3. The requirements for implant materials can be classified into three aspects: the biocompatibility of the material with the human body, the corrosion resistance of the material in the human environment, and the mechanical properties of the material.

Matters needing attention for titanium tube processing?

The workability of titanium alloy is 20-40% of that of 45# steel, and the hardness is less than HB300, which will cause a strong sticking phenomenon; HB>370 is too hard to make processing difficult, and it is best to process titanium alloy with hardness HB300-370. The main reasons that affect its machinability are briefly described as follows: 1) Gas impurities (oxygen, nitrogen, hydrogen, etc.) have a great impact on the machinability of titanium alloys because titanium has high chemical activity and is easy to combine with gas impurities. When the temperature exceeds 600 degrees, titanium is oxidized to form an embrittlement layer, the so-called "structure alpha layer"; it produces hydrogen embrittlement with hydrogen, and forms hard and brittle TiN with nitrogen at high temperatures. 2) The plasticity of titanium alloy is small, which obviously affects its plastic deformation during cutting. The deformation coefficient of titanium alloy is only 1 or even less than 1, while the deformation coefficient of ordinary carbon steel is about 3. During cutting, the chip has a very small contact surface with the rake face, which makes the contact area pressure and the local temperature high, and the tool wears quickly. 3) Severe work hardening occurs when titanium alloy is processed
Ti 7Al-4Mo Titanium Bar      Gr23 Ti-6Al-4V ELI Titanium Plate      ERTi-9 Titanium Welding Wire      F2 Pure Titanium Forging